Laserfiche WebLink
Example of Toter cart bodies made with <br />rotationally molded resin <br />polyethylene <br />NSF <br />Resin <br />Hexene Copolymer LLDPE Rotational Molding Resin <br />Melt Index(3) <br />Density <br />Melting Point (DSC) <br />Flexural Modulus <br />Yield Strength <br />Elongation at Yield <br />ESCR, (F50) <br />Heat Distortion Temperature <br />- 66 psi (4.64 kg/cm') <br />- 264 psi (18.56 kg/cm2) <br />ARM Low Temperature Impact <br />- 0.125" (3.17 mm) <br />- 0.250" (6.35 mm) <br />D 1238 7.0 g/10 min <br />D 792 0.935 g/cm3 <br />METRIC UNITS ENGLISH UNITS <br />125 °C <br />257 <br />°F <br />(4) D 790 <br />680 MPa <br />98,600 <br />psi <br />(5) D 638 <br />17.1 MPa <br />2,500 <br />psi <br />(5) D 638 <br />12 % <br />12 <br />% <br />(6) D 1693 <br />> 1 000 h <br />D 648 58 °C <br />D 648 42 °C <br />(7) <br />ARM Method 68 J <br />ARM Method 203 J <br />136 °F <br />108 °F <br />50 ft-lb <br />150 ft-lb <br />(1) Properties designated have been determined using methods which are in accordance with, or substantially in accordance with, <br />the specified testing standards. <br />(2) Typical Values represent average laboratory values and are intended as guides only, not as specifications. <br />(3) Condition 190°C/2.16 kg. <br />(4) 1 % Strain Value. From compression molded samples. <br />(5) Type IV specimen, 2" (50.8 mm) per minute test speed, 0.075" (1.9 mm) thickness compression molded samples. <br />(6) Condition A & B, 100% IGEPAL, 50°C, F50 values. From compression molded specimens. <br />(7) -40°C on rotomolded samples. <br />Features <br />• Good impact properties <br />• Excellent processability <br />• NSF listed for <br />Standards #24, 51, 61 <br />• UL 94 HB <br />Additives <br />• Processing antioxidant <br />• UV stabilizer <br />Applications <br />• Toys <br />• Complex custom parts <br />• Home and garden items <br />• Mailboxes <br />