Laserfiche WebLink
For more information and technical <br />assistance contact: <br />Chevron Phillips Chemical Company LP <br />P.O. Box 4910 <br />AUNEXv <br />The Woodlands, TX 77387-4910 <br />800.231.1212 POIYFTNYI f Nf <br />PREMIUM EXTRUSION AND RIGID PACKAGING RESINS <br />Marlex° 9005 Polyethylene <br />HIGH DENSITY POLYETHYLENE (HDPE) <br />This high density polyethylene is an ethylene-hexene This resin meets these specifications: <br />copolymer that is tailored for injection molded applications • ASTM D4976 - PE 233 <br />that: • FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H <br />• Require moderate flow per 21 CFR 176.170(c) <br />• Require excellent impact strength • UL94HB yellow card per UL file EE349283 <br />• Require excellent ESCR <br />• Require good warpage resistance <br />• Are durable and recyclable for sustainability <br />Typical injection molded applications for 9005 include: <br />• Industrial parts <br />• Seats <br />• Food and household containers <br />• Agricultural parts <br />Density <br />Melt Index, 190 °C/2.16 kg <br />Tensile Strength at Yield, 2 in/min, Type IV bar <br />Elongation at Break, 2 in/min, Type IV bar <br />Flexural Modulus, Tangent - 16:1 span:depth, 0.5 in/min <br />ESCR, Condition B (100 % Igepal), Fao <br />Durometer Hardness, Type D (Shore D) <br />Vicat Softening Temperature, Loading 1, Rate A <br />Brittleness Temperature, Type A, Type I specimen <br />--- <br />0.945 g/cm3 <br />ASTM D1505 <br />--- <br />6.0 g/10 min <br />ASTM D1238 <br />3,400 psi <br />23 MPa <br />ASTM D638 <br />1,000 % <br />1,000 % <br />ASTM D638 <br />155,000 psi <br />1,070 MPa <br />ASTM D790 <br />90 h <br />90 h <br />ASTM D1693 <br />62 <br />62 <br />ASTM D2240 <br />250 °F <br />121 °C <br />ASTM D1525 <br />< -103 °F <br />< -75 °C <br />ASTM D746 <br />1. The nominal properties reported herein are typical of the product, but do not reflect normal testing variance and therefore should not be used for <br />specification purposes. Values are rounded. The physical properties were determined on compression molded specimens that were prepared in <br />accordance with Procedure C of ASTM D4703, Annex Al. <br />Revision Date: August, 2016 <br />Anot6erquufiryprodudfrom <br />Before using this product, the user is advised and cautioned to make its own determination and assessment of the safety and <br />suitability of the product for the specific use in question and is further advised against relying on the information contained <br />Ch@YIwh <br />herein as it may relate to any specific use or application. It is the ultimate responsibility of the user to ensure that the product is <br />suited and the information is applicable to the user's specific application. Chevron Phillips Chemical Company LP does not <br />make, and expressly disclaims, all warranties, including warranties of merchantability or fitness for a particular purpose, <br />phi��o <br />regardless of whether oral or written, express or implied, or allegedly arising from any usage of any trade or from any course of <br />dealing in connection with the use of the information contained herein or the product itself. The user expressly assumes all risk <br />Cbsmkal Company LP <br />and liability, whether based in contract, tort or otherwise, in connection with the use of the information contained herein or the <br />TheWoodlonds, Texos <br />product itself. Further, information contained herein is given without reference to any intellectual property issues, as well as <br />federal, state or local laws which may be encountered in the use thereof. Such questions should be investigated by the user. <br />Page 1 of 1 <br />