Laserfiche WebLink
TI-0338-A <br />NOVAPOL° POLYETHYLENE MDPE <br />Product Data Sheet Melt Index 3.5 Z <br />Rotational Molding Resin Density 0.938 <br />FEATURES: ADDITIVES: APPLICATIONS: <br />• Hexene copolymer Processing antioxidants Large parts <br />• Excellent impact • Agricultural storage tanks <br />• Excellent ESCR <br />Properties <br />Melt Index (3) <br />ASTM (1) <br />D 1238 <br />Typical Values (2) <br />SI Units English Units <br />3.5 g/10 min <br />MO <br />Densitv <br />D 792 <br />0.938 g/cm' <br />Melting Point <br />129 °C <br />264 °F <br />Crystallization Temperature <br />114 °C <br />237 °F <br />% Crystallinity <br />56 % <br />56 % <br />Molded Plaque Properties <br />Tensile Strength @ Yield <br />D 638 <br />20.6 MPa <br />3 000 psi <br />Tensile Strength @ Break <br />D 638 29.1 <br />MPa 4200 <br />Elongation @ Yield <br />D 638 <br />12 % <br />12 % <br />Elongation @ Break <br />D 638 <br />1 000 % <br />1 000 % <br />Flexural Modulus <br />D 790 <br />702 MPa <br />102 000 psi <br />Izod Impact Resistance (4) <br />D 256 <br />182 J/m <br />3.4 ft-lb/in <br />Tensile Impact Strength <br />D 1822 <br />145 kJ/m' <br />69A ft-Ib/in2 <br />ARM Impact (5) <br />74.5 J/m <br />55 ft-lb/in <br />Softening Point (Vicat) <br />D 1525 <br />122 °C <br />252 °F <br />Heat Deflection Temperature (6) <br />D 648 <br />58 °C <br />136 °F <br />ESCR, F5o 100% IGEPAL(7) <br />D 1693 <br />>1 000 hr <br />>1 000 hr <br />ESCR, F5o 10% IGEPAL (7) <br />D 1693 <br />30 hr <br />30 hr <br />(1) Properties designated have been determined in accordance with the current issues of the specified testing methods <br />Methods of the American Society for Testing and Materials (ASTM) are used wherever applicable. <br />(2) Typical Values represent average laboratory values and are intended as guides only, not as specifications. <br />(3) Condition 190/2,16. <br />(4) 125 mil sample, notched. <br />(5) Association of Rotational Molders, -40°C, 3.2 mm (0.125 in). <br />(6) @ 66 psi. <br />(7) Environmental stress crack resistance, Condition A. <br />.J NOVA Chemicals° ROT''�' <br />